A multicomponent Al84Y9Ni4Co1.5Fe0.5Pd1 alloy was found to keep a mixed glassy + Al phases in the relatively large ribbon thickness range up to about 200 μm for the melt-spun ribbon and in the diameter range up to about 1100 μm for the wedge-shape cone rod prepared by injection copper mold casting. The knowledge of forming Al + glassy phases with high hardness in the wide solidification and annealing conditions through high stability up to complete crystallization for the multicomponent alloy is promising for future development of a high-strength Al-based bulk alloy.