Influence of Ag replacement on supercooled liquid region and icosahedral phase precipitation of Zr65Al7.5Ni10Cu17.5-xAgx (x = 0–17.5 at%) glassy alloys　

The glass transition phenomenon for Zr65Al7.5Ni10Cu17.5-xAgx (x = 5–17.5 at%) glassy alloys was observed in the Ag content range below about 15% and the icosahedral phase precipitated as the heating-induced primary phase in the limited Ag content range.
1712-1721

Journal of Alloys and Compounds