Compositional influence on heating-induced clustered glass formation for multicomponent Zr55-60Al10(Co,Ni,Cu,Ag)30-35 alloys　

The compositional influence on the formation of a clustered glassy structure was examined for Zr-based metallic glasses with multicomponent compositions of Zr60Al10Co30-x (Ni, Cu, Ag)x (x = 5–20, at.%) and Zr55Al10Co10Ni10Cu10Ag5 subjected to long-time annealing at the temperatures above the first-stage crystallization peak temperature (Tp1).
107233

Intermetallics