High formability of glass plus fcc-Al phases in rapidly solidified Al-based multicomponent alloy
|
共著
|
|
|
A multicomponent Al84Y9Ni4Co1.5Fe0.5Pd1 alloy was found to keep a mixed glassy + Al phases in the relatively large ribbon thickness range up to about 200 μm for the melt-spun ribbon and in the diameter range up to about 1100 μm for the wedge-shaped cone rod prepared by injection copper mold casting.
PP 1246-1254
|
Journal of Materials Science
|
|
|
|
|
|
2016/11
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|